Nylon 1313 resin is good at low intensity and water absoption, good reliablity and flexibility even in the low temperature because of its special molecular structuresuper carbon chain and it will be made not only to many types of tubes and coats of proof-oil, pressure, low temperature and high flexility, but also to transparent precision gears and parts of wear resistance. Moreover, it will be processed to the quality film owing to its good air tightness, and will be sprayed directly to the metal surfaces as a ware resistance coat or be drawn to many types of fiber products of high flexbility and wear resistance.
Item |
Unit |
Test method |
Result |
Density |
g/cm3 |
GB1033-86 |
1.02 |
Melting point |
°C |
ASTMD3418-97 |
170 |
Water absorption |
% |
GB1034-86 |
0.2 |
Heat distrotion temperature |
°C |
GB1634-79 |
50 |
Tensile strength |
MPa |
GB/T1040-92 |
45 |
Breaking elongation |
% |
GB/T1040-92 |
300 |
Charpy impact strength |
KJ/m2 |
GB/T1043-93 |
no breakage |
Charpy impact strength(Unnotched) |
KJ/m2 |
GB1043-93 |
26 |
Flexural strength |
MPa |
GB9341-88 |
25 |
Charpy impact strength -40 |
KJ/m2 |
GB/T1043-93 |
no breakage |
Charpy impact strength(Unnotched,-40) |
KJ/m2 |
GB/T1043-93 |
16 |
Shaping shrinkage ratio |
% |
GB1404-86 |
0.5 |
Volume resistivity |
Ω·m |
GB1410-89 |
1.9×1012 |
Dielectric strength |
MV/m |
GB1408-89 |
23.6 |
Dielectric constant(106HZ) |
|
GB1409-88 |
5.59 |
Dielectric loss tangent(106HZ) |
|
GB1409-88 |
0.019 |
Note: Test temperature: 25°C Humidity: 45%
|